ON THE SELECTION OF STEEL ALLOYS FOR CORROSIVE SERVICE D. G. Bellow and I. Smuga - Otto Department of Mechanical ... An electrochemical testing program was developed to evaluate the corrosion resistance of steel alloys used in sucker ...
ON THE SELECTION OF STEEL ALLOYS FOR CORROSIVE SERVICE D. G. Bellow and I. Smuga - Otto Department of Mechanical ... An electrochemical testing program was developed to evaluate the corrosion resistance of steel alloys used in sucker ...
Page 200
All tests were performed in a 1000 ml glass ASTM standard corrosion cell using a 273 EG & G potentiostat / galvanostat with ... It is evident that a better understanding of the corrosion and corrosive - fatigue behaviour of commercially ...
All tests were performed in a 1000 ml glass ASTM standard corrosion cell using a 273 EG & G potentiostat / galvanostat with ... It is evident that a better understanding of the corrosion and corrosive - fatigue behaviour of commercially ...
Page 202
ACKNOWLEDGEMENT corrosion in a deareated 8 % NaC1 / CO2 environment , and further anodically activated by a potentiodynamic scan rate of lmv / sec to the 5000 mA / cm2 current and returned to Ecorr . The pitting depths were measured ...
ACKNOWLEDGEMENT corrosion in a deareated 8 % NaC1 / CO2 environment , and further anodically activated by a potentiodynamic scan rate of lmv / sec to the 5000 mA / cm2 current and returned to Ecorr . The pitting depths were measured ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
OFFSHORE MECHANICS | 1 |
MATERIALS TECHNOLOGY | 9 |
The Plate Thickness Effect in Fatigue Predictions and Results A Review of Norwegian Work | 21 |
Copyright | |
51 other sections not shown
Other editions - View all
Common terms and phrases
alloys analysis applied attachment base behaviour bending calculated carried chord compared composite Conference constant corrosion crack growth curve cycles depth determined developed distribution element energy Engineering environment equation experimental fabrication failure fatigue crack growth fatigue strength field Figure fracture fracture mechanics function geometry given grade heat higher improved increase indicated influence initiation International length load lower material mean measured Mechanics method normal observed obtained Offshore performed pipe pitting plate predicted presented pressure procedure production propagation properties range ratio reduced reference relation reported resistance samples shown shows similar solution specimens standard steel strain strength stress intensity factor stress range structure surface Table temperature tensile thickness effect toughness tubular joints values wall weld metal weld toe welded joints yield
Bibliographic information
| Title | Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3; Volume 8, Part 3 |
| Contributor | American Society of Mechanical Engineers. Offshore Mechanics and Arctic Engineering Division |
| Publisher | American Society of Mechanical Engineers, 1989 |
| Original from | the University of Michigan |
| Digitized | 4 Dec 2007 |
| Export Citation | BiBTeX EndNote RefMan |