Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3; Volume 8, Part 3American Society of Mechanical Engineers, 1989 - Arctic regions |
From inside the book
Results 1-3 of 77
Page 71
... ( lower yield strength 1 side of the joint ) and 6 , ( overmatching side of the 2 joint ) . Following the procedure given in [ 2 ] different rotational factors can be determined for the lower- and overmatching yield strength side of the ...
... ( lower yield strength 1 side of the joint ) and 6 , ( overmatching side of the 2 joint ) . Following the procedure given in [ 2 ] different rotational factors can be determined for the lower- and overmatching yield strength side of the ...
Page 72
... lower bound transition curve needs post test exa- mination of the specimens tested . In Fig . 12 lower bound curves are given for V - notched and fatigue - cracked HAZ specimens . As a criterion for lower bound it was required that for ...
... lower bound transition curve needs post test exa- mination of the specimens tested . In Fig . 12 lower bound curves are given for V - notched and fatigue - cracked HAZ specimens . As a criterion for lower bound it was required that for ...
Page 672
Assessment of fracture analysis methods ( Burst tests and wide plate tests ) Applicability Lower shelf Transition region Upper shelf Lower shelf Transition region Upper shelf Accuracy Safety Level of sophistication Costs including ...
Assessment of fracture analysis methods ( Burst tests and wide plate tests ) Applicability Lower shelf Transition region Upper shelf Lower shelf Transition region Upper shelf Accuracy Safety Level of sophistication Costs including ...
Contents
OFFSHORE MECHANICS | 1 |
MATERIALS TECHNOLOGY | 9 |
The Plate Thickness Effect in Fatigue Predictions and Results A Review of Norwegian Work | 21 |
Copyright | |
51 other sections not shown
Other editions - View all
Common terms and phrases
alloy aluminum analysis applied Arctic Engineering ASTM austenite axial base metal behaviour bending brace calculated cathodic protection Charpy chord Conference on Offshore corrosion fatigue crack depth crack growth rate crack initiation crack propagation crevice corrosion CTOD da/dN defects developed equation experimental fabrication fatigue crack growth fatigue strength fatigue test ferrite Figure fillet welds finite element fracture mechanics fracture toughness geometry grade heat input heat treatment HSLA steels increase influence kJ/cm load material mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics offshore structures parameters pipe pitting plate thickness predicted procedure PWHT ratio reduced reheated S-N curves seawater Shoralsim shown in Fig solution specimens Steel in Marine strain stress concentration stress intensity factor stress range submerged arc welding surface crack T-joints Table temperature tensile thickness effect tubular joints values weld metal weld profile weld toe weldability welded joints yield strength