... lower bound to the scatter band is best represented by ( to / t ) . although it should be noted that restricting the lower limit to 22 mm does not take into account the improved fatigue life at lower thicknesses . This latter point is ...
... lower bound to the scatter band is best represented by ( to / t ) . although it should be noted that restricting the lower limit to 22 mm does not take into account the improved fatigue life at lower thicknesses . This latter point is ...
Page 71
... ( lower yield strength 1 side of the joint ) and 62 ( overmatching side of the joint ) . Following the procedure given in [ 2 ] different rotational factors can be determined for the lower- and overmatching yield strength side of the ...
... ( lower yield strength 1 side of the joint ) and 62 ( overmatching side of the joint ) . Following the procedure given in [ 2 ] different rotational factors can be determined for the lower- and overmatching yield strength side of the ...
Page 72
... lower bound transition curve needs post test exa- mination of the specimens tested . In Fig . 12 lower bound curves are given for V - notched and fatigue - cracked HAZ specimens . As a criterion for lower bound it was required that for ...
... lower bound transition curve needs post test exa- mination of the specimens tested . In Fig . 12 lower bound curves are given for V - notched and fatigue - cracked HAZ specimens . As a criterion for lower bound it was required that for ...
Contents
OFFSHORE MECHANICS | 1 |
MATERIALS TECHNOLOGY | 9 |
The Plate Thickness Effect in Fatigue Predictions and Results A Review of Norwegian Work | 21 |
Copyright | |
50 other sections not shown
Other editions - View all
Common terms and phrases
alloy aluminum analysis applied Arctic Engineering ASTM austenite axial base metal behaviour bending brace calculated cathodic protection Charpy chord Conference on Offshore corrosion fatigue crack depth crack growth rate crack initiation crack propagation crevice corrosion CTOD da/dN defects developed energy environment equation experimental fabrication fatigue crack growth fatigue strength fatigue test ferrite Figure fillet welds finite element fracture mechanics fracture toughness geometry grade heat input heat treatment HSLA steels increase influence kJ/cm load material mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics offshore structures parameters pipe pitting plate thickness predicted procedure PWHT ratio reduced S-N curves seawater Shoralsim shown in Fig solution specimens Steel in Marine strain stress concentration stress intensity factor stress range submerged arc welding surface crack T-joints Table temperature tensile thickness effect tubular joints values weld metal weld profile weld toe weldability welded joints yield strength