Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3; Volume 8, Part 3American Society of Mechanical Engineers, 1989 - Arctic regions |
From inside the book
Results 1-3 of 72
Page 223
... performed on ISO - V test specimens . Toughness tests of thermally aged samples were performed using ISO - V test specimens machined from samples aged in the laboratory furnace followed by water quenching . Pitting corrosion behaviour ...
... performed on ISO - V test specimens . Toughness tests of thermally aged samples were performed using ISO - V test specimens machined from samples aged in the laboratory furnace followed by water quenching . Pitting corrosion behaviour ...
Page 272
... performed at 550 ° C . MECHANICAL PROPERTIES OF PLATE Table 3 shows the mechanical properties of the plate . Yield and tensile strengths were above 510 and 590 MPa , respectively and the 50 % FATT was lower than -90 ° C . The post- weld ...
... performed at 550 ° C . MECHANICAL PROPERTIES OF PLATE Table 3 shows the mechanical properties of the plate . Yield and tensile strengths were above 510 and 590 MPa , respectively and the 50 % FATT was lower than -90 ° C . The post- weld ...
Page 367
... performed with an adapted filler metal on 30 and 50 millimeters thick plates ( Table 12 ) . HAZ Distance WELDED JOINT ( transvers direction ) Y.S.0.2 U.T.S. Rupture from Samplings were realized in both base metal and heat affected zone ...
... performed with an adapted filler metal on 30 and 50 millimeters thick plates ( Table 12 ) . HAZ Distance WELDED JOINT ( transvers direction ) Y.S.0.2 U.T.S. Rupture from Samplings were realized in both base metal and heat affected zone ...
Contents
OFFSHORE MECHANICS | 1 |
MATERIALS TECHNOLOGY | 9 |
The Plate Thickness Effect in Fatigue Predictions and Results A Review of Norwegian Work | 21 |
Copyright | |
50 other sections not shown
Other editions - View all
Common terms and phrases
alloy aluminum analysis applied Arctic Engineering ASTM austenite axial base metal behaviour bending brace calculated cathodic protection Charpy chord Conference on Offshore corrosion fatigue crack depth crack growth rate crack initiation crack propagation crevice corrosion CTOD da/dN defects developed energy environment equation experimental fabrication fatigue crack growth fatigue strength fatigue test ferrite Figure fillet welds finite element fracture mechanics fracture toughness geometry grade heat input heat treatment HSLA steels increase influence kJ/cm load material mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics offshore structures parameters pipe pitting plate thickness predicted procedure PWHT ratio reduced S-N curves seawater Shoralsim shown in Fig solution specimens Steel in Marine strain stress concentration stress intensity factor stress range submerged arc welding surface crack T-joints Table temperature tensile thickness effect tubular joints values weld metal weld profile weld toe weldability welded joints yield strength