Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3; Volume 8, Part 3American Society of Mechanical Engineers, 1989 - Arctic regions |
From inside the book
Results 1-3 of 76
Page 22
... shown graphs for weld root and toe failure analysis respectively . As shown , the value of k is given as a function of plate thickness , leading to a detrimental effect of plate thickness . con- When the DnV approach was introduced ...
... shown graphs for weld root and toe failure analysis respectively . As shown , the value of k is given as a function of plate thickness , leading to a detrimental effect of plate thickness . con- When the DnV approach was introduced ...
Page 23
... shown experimentally and by fracture mechancis ana- lysis by Maddox ( 1987 ) the elastic stress con- centration at the weld toe of a transverse fillet weld depends on the thickness of the attachment . The thickness effect may therefore ...
... shown experimentally and by fracture mechancis ana- lysis by Maddox ( 1987 ) the elastic stress con- centration at the weld toe of a transverse fillet weld depends on the thickness of the attachment . The thickness effect may therefore ...
Page 24
... shown in Fig . 14. Again the thickness correction curve provides a satisfactory fit to the data . Sea water and cathodic protection . The series shown in Fig . 13 were also tested in sea water with cathodic protection by Berge et al ...
... shown in Fig . 14. Again the thickness correction curve provides a satisfactory fit to the data . Sea water and cathodic protection . The series shown in Fig . 13 were also tested in sea water with cathodic protection by Berge et al ...
Contents
OFFSHORE MECHANICS | 1 |
MATERIALS TECHNOLOGY | 9 |
The Plate Thickness Effect in Fatigue Predictions and Results A Review of Norwegian Work | 21 |
Copyright | |
50 other sections not shown
Other editions - View all
Common terms and phrases
alloy aluminum analysis applied Arctic Engineering ASTM austenite axial base metal behaviour bending brace calculated cathodic protection Charpy chord Conference on Offshore corrosion fatigue crack depth crack growth rate crack initiation crack propagation crevice corrosion CTOD da/dN defects developed energy environment equation experimental fabrication fatigue crack growth fatigue strength fatigue test ferrite Figure fillet welds finite element fracture mechanics fracture toughness geometry grade heat input heat treatment HSLA steels increase influence kJ/cm load material mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics offshore structures parameters pipe pitting plate thickness predicted procedure PWHT ratio reduced S-N curves seawater Shoralsim shown in Fig solution specimens Steel in Marine strain stress concentration stress intensity factor stress range submerged arc welding surface crack T-joints Table temperature tensile thickness effect tubular joints values weld metal weld profile weld toe weldability welded joints yield strength