Page 11
... shows that parallel straight lines do not provide the best fit for the data . The data would be better described by a set of lines with decreasing negative slope m for thicker joints . This decreasing slope , which would result in a ...
... shows that parallel straight lines do not provide the best fit for the data . The data would be better described by a set of lines with decreasing negative slope m for thicker joints . This decreasing slope , which would result in a ...
Page 156
... shows the modeling of tubular joint with a fillet and the surface crack is located at the hot spot under the inplane bending moment . Figure 8 shows the mixed mode stress intensity factor distribution of a tubular joint with a surface ...
... shows the modeling of tubular joint with a fillet and the surface crack is located at the hot spot under the inplane bending moment . Figure 8 shows the mixed mode stress intensity factor distribution of a tubular joint with a surface ...
Page 651
... shows the CTOD transition curve . Even at -50 ° C , base plate achived high resistance against brittle fracture initiation . Table 5 shows drop - weight test results on surface and 1 / 2t locations . The nil - ductility transition ...
... shows the CTOD transition curve . Even at -50 ° C , base plate achived high resistance against brittle fracture initiation . Table 5 shows drop - weight test results on surface and 1 / 2t locations . The nil - ductility transition ...
Contents
OFFSHORE MECHANICS | 1 |
MATERIALS TECHNOLOGY | 9 |
The Plate Thickness Effect in Fatigue Predictions and Results A Review of Norwegian Work | 21 |
Copyright | |
50 other sections not shown
Other editions - View all
Common terms and phrases
alloy aluminum analysis applied Arctic Engineering ASTM austenite axial base metal behaviour bending brace calculated cathodic protection Charpy chord Conference on Offshore corrosion fatigue crack depth crack growth rate crack initiation crack propagation crevice corrosion CTOD da/dN defects developed energy environment equation experimental fabrication fatigue crack growth fatigue strength fatigue test ferrite Figure fillet welds finite element fracture mechanics fracture toughness geometry grade heat input heat treatment HSLA steels increase influence kJ/cm load material mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics offshore structures parameters pipe pitting plate thickness predicted procedure PWHT ratio reduced S-N curves seawater Shoralsim shown in Fig solution specimens Steel in Marine strain stress concentration stress intensity factor stress range submerged arc welding surface crack T-joints Table temperature tensile thickness effect tubular joints values weld metal weld profile weld toe weldability welded joints yield strength