Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3; Volume 8, Part 3American Society of Mechanical Engineers, 1989 - Arctic regions |
From inside the book
Results 1-3 of 79
Page 71
... specimens , the CTOD values were also determined following a modified formula suggested by Toyoda et al [ 2 ] . Stot ... specimens taken from the root run areas of the double side welded joints . Differences in metallurgical composition ...
... specimens , the CTOD values were also determined following a modified formula suggested by Toyoda et al [ 2 ] . Stot ... specimens taken from the root run areas of the double side welded joints . Differences in metallurgical composition ...
Page 73
... specimens will fail by cleavage whereas subsurface specimens will show ductile frac- ture behaviour in the CTOD tests at -50 ° C . As can be seen from the results in Fig . 15 root run specimens failed by cleavage and subsurface specimens ...
... specimens will fail by cleavage whereas subsurface specimens will show ductile frac- ture behaviour in the CTOD tests at -50 ° C . As can be seen from the results in Fig . 15 root run specimens failed by cleavage and subsurface specimens ...
Page 441
... specimens . Figure 6 shows results for all specimens tested at 240 MPa hot - spot stress , and Figure 7 those tested at 160 MPa hot - spot stress . The crack growth rates in seawater with free corrosion were consistently higher than ...
... specimens . Figure 6 shows results for all specimens tested at 240 MPa hot - spot stress , and Figure 7 those tested at 160 MPa hot - spot stress . The crack growth rates in seawater with free corrosion were consistently higher than ...
Contents
OFFSHORE MECHANICS | 1 |
MATERIALS TECHNOLOGY | 9 |
The Plate Thickness Effect in Fatigue Predictions and Results A Review of Norwegian Work | 21 |
Copyright | |
51 other sections not shown
Other editions - View all
Common terms and phrases
alloy aluminum analysis applied Arctic Engineering ASTM austenite axial base metal behaviour bending brace calculated cathodic protection Charpy chord Conference on Offshore corrosion fatigue crack depth crack growth rate crack initiation crack propagation crevice corrosion CTOD da/dN defects developed equation experimental fabrication fatigue crack growth fatigue strength fatigue test ferrite Figure fillet welds finite element fracture mechanics fracture toughness geometry grade heat input heat treatment HSLA steels increase influence kJ/cm load material mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics offshore structures parameters pipe pitting plate thickness predicted procedure PWHT ratio reduced reheated S-N curves seawater Shoralsim shown in Fig solution specimens Steel in Marine strain stress concentration stress intensity factor stress range submerged arc welding surface crack T-joints Table temperature tensile thickness effect tubular joints values weld metal weld profile weld toe weldability welded joints yield strength