Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 3; Volume 8, Part 3American Society of Mechanical Engineers, 1989 - Arctic regions |
From inside the book
Results 1-3 of 82
Page 322
... tensile test and yield to tensile ratio Yield to tensile ratio , YR ( % ) 100 Q & T steel 90 80 910 ° C Q⭑T о бој Øy ει log & ( a ) Logo - logɛ relation with Luders ' strain 500 600 700 800 900 1000 Tensile strength , or ( MPa ) Fig ...
... tensile test and yield to tensile ratio Yield to tensile ratio , YR ( % ) 100 Q & T steel 90 80 910 ° C Q⭑T о бој Øy ει log & ( a ) Logo - logɛ relation with Luders ' strain 500 600 700 800 900 1000 Tensile strength , or ( MPa ) Fig ...
Page 328
... tensile ratio of the steel . It is an important question which level of yield to tensile ratio is most appropriate . There are considerable difficulties for determining that level , since the deformability is not necessarily considered ...
... tensile ratio of the steel . It is an important question which level of yield to tensile ratio is most appropriate . There are considerable difficulties for determining that level , since the deformability is not necessarily considered ...
Page 633
... tensile properties of the base metal , the weld metal and the junction between weld and base plate ( heat affected zone ) when the weldment is subjected to external forces . For examp- le , if some defect / crack is present in amounts ...
... tensile properties of the base metal , the weld metal and the junction between weld and base plate ( heat affected zone ) when the weldment is subjected to external forces . For examp- le , if some defect / crack is present in amounts ...
Contents
OFFSHORE MECHANICS | 1 |
MATERIALS TECHNOLOGY | 9 |
The Plate Thickness Effect in Fatigue Predictions and Results A Review of Norwegian Work | 21 |
Copyright | |
50 other sections not shown
Other editions - View all
Common terms and phrases
alloy aluminum analysis applied Arctic Engineering ASTM austenite axial base metal behaviour bending brace calculated cathodic protection Charpy chord Conference on Offshore corrosion fatigue crack depth crack growth rate crack initiation crack propagation crevice corrosion CTOD da/dN defects developed energy environment equation experimental fabrication fatigue crack growth fatigue strength fatigue test ferrite Figure fillet welds finite element fracture mechanics fracture toughness geometry grade heat input heat treatment HSLA steels increase influence kJ/cm load material mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics offshore structures parameters pipe pitting plate thickness predicted procedure PWHT ratio reduced S-N curves seawater Shoralsim shown in Fig solution specimens Steel in Marine strain stress concentration stress intensity factor stress range submerged arc welding surface crack T-joints Table temperature tensile thickness effect tubular joints values weld metal weld profile weld toe weldability welded joints yield strength