... weld metal ( Fig . 10 ) . Since the change in loading conditions , caused by the presence of a sharp crack instead of a blunt notch , is the same for both weld metal speci- men types the difference in transition temperature shifts can ...
... weld metal ( Fig . 10 ) . Since the change in loading conditions , caused by the presence of a sharp crack instead of a blunt notch , is the same for both weld metal speci- men types the difference in transition temperature shifts can ...
Page 489
... welding process on C - Mn weld metal microstructure and mechanical properties is investigated . The microstructure of the as - deposited weld metal is assessed quantitatively in terms of grain boundary ferrite ( GF ) , ferrite with ...
... welding process on C - Mn weld metal microstructure and mechanical properties is investigated . The microstructure of the as - deposited weld metal is assessed quantitatively in terms of grain boundary ferrite ( GF ) , ferrite with ...
Page 633
... plastic strains . On All weld metal tension tests are more suitable is to provide information on the actual degree of weld The Hague 633 - March 19-23 , 1989 Weld Metal Yield Strength Requirements and High Strength Steels R Denys and T ...
... plastic strains . On All weld metal tension tests are more suitable is to provide information on the actual degree of weld The Hague 633 - March 19-23 , 1989 Weld Metal Yield Strength Requirements and High Strength Steels R Denys and T ...
Contents
OFFSHORE MECHANICS | 1 |
MATERIALS TECHNOLOGY | 9 |
The Plate Thickness Effect in Fatigue Predictions and Results A Review of Norwegian Work | 21 |
Copyright | |
50 other sections not shown
Other editions - View all
Common terms and phrases
alloy aluminum analysis applied Arctic Engineering ASTM austenite axial base metal behaviour bending brace calculated cathodic protection Charpy chord Conference on Offshore corrosion fatigue crack depth crack growth rate crack initiation crack propagation crevice corrosion CTOD da/dN defects developed energy environment equation experimental fabrication fatigue crack growth fatigue strength fatigue test ferrite Figure fillet welds finite element fracture mechanics fracture toughness geometry grade heat input heat treatment HSLA steels increase influence kJ/cm load material mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics offshore structures parameters pipe pitting plate thickness predicted procedure PWHT ratio reduced S-N curves seawater Shoralsim shown in Fig solution specimens Steel in Marine strain stress concentration stress intensity factor stress range submerged arc welding surface crack T-joints Table temperature tensile thickness effect tubular joints values weld metal weld profile weld toe weldability welded joints yield strength