... weld ( mm ) ( mm ) ( deg ) ( deg ) ( deg ) | ( deg ) | ( deg ) Fig . 10 Predicted thickness effect by models using multiple. Joint identification 52 / 52-100 ... weld toe cracks . cance of this phenomenon or its incorporation into crack - 14.
... weld ( mm ) ( mm ) ( deg ) ( deg ) ( deg ) | ( deg ) | ( deg ) Fig . 10 Predicted thickness effect by models using multiple. Joint identification 52 / 52-100 ... weld toe cracks . cance of this phenomenon or its incorporation into crack - 14.
Page 22
... welds , i.e. welds free from macroscopic defects , fatigue cracks will in general be initiated along the weld toe . A useful model for describing the thickness effect in weld toe fatigue failures is obtained by the following assumptions ...
... welds , i.e. welds free from macroscopic defects , fatigue cracks will in general be initiated along the weld toe . A useful model for describing the thickness effect in weld toe fatigue failures is obtained by the following assumptions ...
Page 43
... weld was decreased . In practice , in order to improve the weld profile , the throat will remain constant and the weld toe will be moved further away from the joint by the addition of weld metal . In addition to reducing the stress ...
... weld was decreased . In practice , in order to improve the weld profile , the throat will remain constant and the weld toe will be moved further away from the joint by the addition of weld metal . In addition to reducing the stress ...
Contents
OFFSHORE MECHANICS | 1 |
MATERIALS TECHNOLOGY | 9 |
The Plate Thickness Effect in Fatigue Predictions and Results A Review of Norwegian Work | 21 |
Copyright | |
50 other sections not shown
Other editions - View all
Common terms and phrases
alloy aluminum analysis applied Arctic Engineering ASTM austenite axial base metal behaviour bending brace calculated cathodic protection Charpy chord Conference on Offshore corrosion fatigue crack depth crack growth rate crack initiation crack propagation crevice corrosion CTOD da/dN defects developed energy environment equation experimental fabrication fatigue crack growth fatigue strength fatigue test ferrite Figure fillet welds finite element fracture mechanics fracture toughness geometry grade heat input heat treatment HSLA steels increase influence kJ/cm load material mechanical properties Mechanics and Arctic method microstructure notch obtained Offshore Mechanics offshore structures parameters pipe pitting plate thickness predicted procedure PWHT ratio reduced S-N curves seawater Shoralsim shown in Fig solution specimens Steel in Marine strain stress concentration stress intensity factor stress range submerged arc welding surface crack T-joints Table temperature tensile thickness effect tubular joints values weld metal weld profile weld toe weldability welded joints yield strength