Engineering Materials and Their ApplicationsThis edition of the classic text/reference book has been updated and revised to provide balanced coverage of metals, ceramics, polymers and composites. The first five chapters assess the different structures of metals, ceramics and polymers and how stress and temperature affect them. Demonstrates how to optimize a material's structure by using equilibrium data (phase diagrams) and nonequilibrium conditions, especially precipitation hardening. Discusses the structures, characteristics and applications of the important materials in each field. Considers topics common to all materials--corrosion and oxidation, failure analysis, processing of electrical and magnetic materials, materials selection and specification. Contains special chapters on advanced and large volume engineering materials plus abundant examples and problems. |
From inside the book
Results 1-3 of 25
Page 190
... Bainite : isothermal holding of austenite below the nose of a TTT diagram . ( Bainite may also be obtained by cooling if two noses are present , with the bainite nose out ahead of the pearlite nose . See Sec . 6.18 and Fig . 6.29 . ) 3 ...
... Bainite : isothermal holding of austenite below the nose of a TTT diagram . ( Bainite may also be obtained by cooling if two noses are present , with the bainite nose out ahead of the pearlite nose . See Sec . 6.18 and Fig . 6.29 . ) 3 ...
Page 191
... bainite at the desired level of the bainite temperature range . The part is first austenitized , quenched in a salt bath above the M ,, allowed to transform , and then air - cooled . Naturally the as - quenched hardness is lower than if ...
... bainite at the desired level of the bainite temperature range . The part is first austenitized , quenched in a salt bath above the M ,, allowed to transform , and then air - cooled . Naturally the as - quenched hardness is lower than if ...
Page 226
... Bainite can be obtained either by an isothermal heat treatment or by casting an alloy combination which produces a TTT curve with a pro- nounced bainite nose . For example , to produce a bainite structure in a 1 - in . - diameter ...
... Bainite can be obtained either by an isothermal heat treatment or by casting an alloy combination which produces a TTT curve with a pro- nounced bainite nose . For example , to produce a bainite structure in a 1 - in . - diameter ...
Other editions - View all
Engineering Materials and Their Applications Richard Aloysius Flinn,Paul K. Trojan Snippet view - 1986 |
Engineering Materials and Their Applications Richard Aloysius Flinn,Paul K. Trojan Snippet view - 1975 |
Engineering Materials and Their Applications Richard Aloysius Flinn,Paul K. Trojan Snippet view - 1975 |
Common terms and phrases
0.8 percent carbon 10-3 to obtain alloys aluminum Annealed anode atoms austenite bainite bonds brittle Calculate carbide cast iron cathode ceramics Chap chemical chromium cold-worked composition cooling copper corrosion crystal curve density diffusion discussed ductile iron effect electrical electron hole electrons elements energy engineering eutectoid example Fe2+ ferrite fibers fracture glass grain graphite H H H hardening hardness heat treatment hydrogen important ions kg/mm² liquid load magnesium magnetic martensite material matrix melt metal microstructure mold molecules nickel oxide oxygen pearlite percent elongation percent silicon phase diagram plane plastic polarization polyethylene polymer polymerization precipitate produced properties quenched reaction resistance semiconductor shown in Fig silica slip sodium solid solution specimen strain stress structure surface Table temper temperature tensile strength thermoplastic thermosetting transformation two-phase typical unit cell valence volume Weight percentage yield strength zinc