Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968K. N. P. Rao, A. K. Lahiri |
From inside the book
Results 1-3 of 7
Page 53
... Company plant and the remedial measures taken . The slurried rock phosphate is pumped to the washer plant through cast iron pipes . The slurried rock is abrasive but not normally corrosive . The greatest wear occurred along the bottom ...
... Company plant and the remedial measures taken . The slurried rock phosphate is pumped to the washer plant through cast iron pipes . The slurried rock is abrasive but not normally corrosive . The greatest wear occurred along the bottom ...
Page 57
... company has prepared synthetic glasses moulded from Kel - F fluorocarbon plastic which can stand temperatures from 65 to 300 ° F and can resist shock and vibration . Even glass coated with high temperature clean plastics such as Teflon ...
... company has prepared synthetic glasses moulded from Kel - F fluorocarbon plastic which can stand temperatures from 65 to 300 ° F and can resist shock and vibration . Even glass coated with high temperature clean plastics such as Teflon ...
Page 96
... Company , New York , 276 , 1958 . U. S. Patent No. 2,042,274 Cook , S. , Proc . A. P. 1. , 32M ( III ) , 72 , 1952 . Derungs , W. A. , Corrosion , 12 , 617t , 1956 . Tait , E. J. M. , Inst . Pet . Rev. , 7 , 66 , 1953 . Garner , E. H. ...
... Company , New York , 276 , 1958 . U. S. Patent No. 2,042,274 Cook , S. , Proc . A. P. 1. , 32M ( III ) , 72 , 1952 . Derungs , W. A. , Corrosion , 12 , 617t , 1956 . Tait , E. J. M. , Inst . Pet . Rev. , 7 , 66 , 1953 . Garner , E. H. ...
Contents
INTRODUCTION | 3 |
CHEMICAL CORROSION AND ITS PREVENTION | 13 |
CORROSION PROBLEMS IN THE MANUFACTURE OF NITROGEN BASED FERTILIZER | 27 |
9 other sections not shown
Common terms and phrases
addition alloys aluminium ammonia ammonium amount anodic application attack bottom carbon steel cast iron cathodic protection cause chemical chloride chromium coatings concentration construction containing cooling corrosion problems corrosion rate cracking crude developed distillation effective environment epoxy equipment exchangers failure fertiliser flow formation give given handling heat higher hydrogen hydrogen sulphide increase industry inhibitor iron lead material metal method mild steel Monel months natural observed occurred operating organic oxide oxygen paint petroleum phosphate pipe pitting plant plates potential practice presence pressure prevent pumps range reaction reduced refinery removal resistance rubber severe shell showing solution specially stainless steel steam storage tanks stress corrosion structure suitable sulphuric acid surface Table tanks temperature tests thickness tower treatment tubes unit various welding zinc