... Hastelloy P - 203 - Slurry Feed Pump ( Vertical type ) a ) Pump case , shaft , liners , suction and casing cover ... Hastelloy - C and sleeve material also Hastelloy - C . Shaft life is about 4 to 5 months . Shaft sleeve life is 1 to 2 ...
... Hastelloy P - 203 - Slurry Feed Pump ( Vertical type ) a ) Pump case , shaft , liners , suction and casing cover ... Hastelloy - C and sleeve material also Hastelloy - C . Shaft life is about 4 to 5 months . Shaft sleeve life is 1 to 2 ...
Page 95
... Hastelloy C or Illium are also used . Ph - 8 % Sb alloy has also been used successfully as pump bodies where separation of oil from sludge is done in high speed centrifugals ; the bowls of these centrifuge are machined from monel ...
... Hastelloy C or Illium are also used . Ph - 8 % Sb alloy has also been used successfully as pump bodies where separation of oil from sludge is done in high speed centrifugals ; the bowls of these centrifuge are machined from monel ...
Page 131
... Hastelloy C ( 62 Ni , 17 Cr , 15 Mo ) ( 18-8 Mo stainless steel ( passive ) ( 18-8 stainless steel ( passive ) ( Chromium stainless steel , 11-30 % Cr ( passive ) ( Inconel ( passive ) ( 80 Ni , 13 Cr , 7 Fe ) ( Nickel ( passive ) ...
... Hastelloy C ( 62 Ni , 17 Cr , 15 Mo ) ( 18-8 Mo stainless steel ( passive ) ( 18-8 stainless steel ( passive ) ( Chromium stainless steel , 11-30 % Cr ( passive ) ( Inconel ( passive ) ( 80 Ni , 13 Cr , 7 Fe ) ( Nickel ( passive ) ...
Contents
INTRODUCTION | 3 |
CHEMICAL CORROSION AND ITS PREVENTION | 13 |
CORROSION PROBLEMS IN THE MANUFACTURE OF NITROGEN BASED FERTILIZER | 27 |
9 other sections not shown
Common terms and phrases
addition alloys aluminium ammonia ammonium amount anodic application attack bottom carbon steel cast iron cathodic protection cause chemical chloride chromium coatings concentration construction containing cooling corrosion problems corrosion rate cracking crude developed distillation effective environment epoxy equipment exchangers failure fertiliser flow formation give given handling heat higher hydrogen hydrogen sulphide increase industry inhibitor iron lead material metal method mild steel Monel months natural observed occurred operating organic oxide oxygen paint petroleum phosphate pipe pitting plant plates potential practice presence pressure prevent pumps range reaction reduced refinery removal resistance rubber severe shell showing solution specially stainless steel steam storage tanks stress corrosion structure suitable sulphuric acid surface Table tanks temperature tests thickness tower treatment tubes unit various welding zinc