Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 |
From inside the book
Results 1-3 of 16
Page 49
Improved life for the pumps handling molten sulphur could be obtained through
the use of sulphuric acid resistant alloys such as duriment rather than cast iron .
The hot gases from the burners are often partially cooled and transported to the ...
Improved life for the pumps handling molten sulphur could be obtained through
the use of sulphuric acid resistant alloys such as duriment rather than cast iron .
The hot gases from the burners are often partially cooled and transported to the ...
Page 50
increased volume of the oxidation product and pressure built up in the confined
areas result in splitting the cast iron . Steel is preferred to cast iron for oleum
service . Cast iron and cast steel valves were , and still are , used for contact acid
.
increased volume of the oxidation product and pressure built up in the confined
areas result in splitting the cast iron . Steel is preferred to cast iron for oleum
service . Cast iron and cast steel valves were , and still are , used for contact acid
.
Page 156
Mr . D . S . Likhari ( Hindustan Zinc Ltd . , Udaipur ) We have faced some
problems with the cast iron moulds used for casting of zinc ingots . We have not
been able to get a life of more than about 1 - 2 months with these moulds . I
would like to ...
Mr . D . S . Likhari ( Hindustan Zinc Ltd . , Udaipur ) We have faced some
problems with the cast iron moulds used for casting of zinc ingots . We have not
been able to get a life of more than about 1 - 2 months with these moulds . I
would like to ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
INTRODUCTION | 3 |
CHEMICAL CORROSION AND ITS PREVENTION | 13 |
DISCUSSION | 22 |
9 other sections not shown
Common terms and phrases
addition alloys aluminium ammonia ammonium amount anodic application attack bottom carbon steel cast iron cathodic protection cause chemical chloride chromium coatings concentration construction containing cooling corrosion problems corrosion rate cracking crude developed distillation effective environment epoxy equipment exchangers failure fertiliser flow give given handling heat hydrogen hydrogen sulphide increase industry inhibitor iron lead less material metal method mild steel Monel months natural observed occurred operating organic oxide oxygen paint petroleum phosphate pipe pitting plant plates potential practice presence pressure prevent pumps range reaction reduced refinery removal resistance rubber severe shell showing solution specially stainless steel steam storage tanks stress corrosion structure suitable sulphuric acid surface Table tanks temperature tests thickness tower treatment tubes unit various welding zinc
Bibliographic information
| Title | Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 |
| Editors | K. N. P. Rao, A. K. Lahiri |
| Contributor | Corrosion Advisory Bureau |
| Publisher | Corrosion Advisory Bureau, 1969 |
| Original from | the University of Wisconsin - Madison |
| Digitized | 27 Feb 2008 |
| Length | 159 pages |
| Export Citation | BiBTeX EndNote RefMan |