Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 |
From inside the book
Results 1-3 of 8
Page 46
A stationary coat of polyester resin was applied to the new concrete base , a
trowel coat of silica filled polyester resin glass was embedded in this coat and a
second trowel coat was applied . Flourney43 has described the use of aluminium
...
A stationary coat of polyester resin was applied to the new concrete base , a
trowel coat of silica filled polyester resin glass was embedded in this coat and a
second trowel coat was applied . Flourney43 has described the use of aluminium
...
Page 118
The protective scheme for storage tanks that have shown longest life , even in
marine conditions , comprises of two coats of red lead graphite primer followed
by two coats of a finishing paint having a total film thickness of at least 5 mils .
The protective scheme for storage tanks that have shown longest life , even in
marine conditions , comprises of two coats of red lead graphite primer followed
by two coats of a finishing paint having a total film thickness of at least 5 mils .
Page 149
The priming coat should be followed either at the workshop or at the site by
number of suitable undercoats and ... Finishing coats and undercoats should be
chosen for their low permeability to moisture and gases present in the
environment .
The priming coat should be followed either at the workshop or at the site by
number of suitable undercoats and ... Finishing coats and undercoats should be
chosen for their low permeability to moisture and gases present in the
environment .
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
INTRODUCTION | 3 |
CHEMICAL CORROSION AND ITS PREVENTION | 13 |
DISCUSSION | 22 |
9 other sections not shown
Common terms and phrases
addition alloys aluminium ammonia ammonium amount anodic application attack bottom carbon steel cast iron cathodic protection cause chemical chloride chromium coatings concentration construction containing cooling corrosion problems corrosion rate cracking crude developed distillation effective environment epoxy equipment exchangers failure fertiliser flow give given handling heat hydrogen hydrogen sulphide increase industry inhibitor iron lead less material metal method mild steel Monel months natural observed occurred operating organic oxide oxygen paint petroleum phosphate pipe pitting plant plates potential practice presence pressure prevent pumps range reaction reduced refinery removal resistance rubber severe shell showing solution specially stainless steel steam storage tanks stress corrosion structure suitable sulphuric acid surface Table tanks temperature tests thickness tower treatment tubes unit various welding zinc
Bibliographic information
| Title | Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 |
| Editors | K. N. P. Rao, A. K. Lahiri |
| Contributor | Corrosion Advisory Bureau |
| Publisher | Corrosion Advisory Bureau, 1969 |
| Original from | the University of Wisconsin - Madison |
| Digitized | 27 Feb 2008 |
| Length | 159 pages |
| Export Citation | BiBTeX EndNote RefMan |