Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 |
From inside the book
Results 1-3 of 23
Page 38
2 % potassium chromate was very effective in absence of HS but in presence of
saturated CO , and H2S sodium metavanadate or vanadium pentoxide were
effective ; complete protection with metavanadate was obtained at a
concentration of ...
2 % potassium chromate was very effective in absence of HS but in presence of
saturated CO , and H2S sodium metavanadate or vanadium pentoxide were
effective ; complete protection with metavanadate was obtained at a
concentration of ...
Page 51
Anodic protection54 has been successfully applied and is effective in controlling
corrosion of mild steel in storage tanks , etc . , in black as well as white
concentrated acids . Behaviour of sulphuric acid has attracted wide attention55 .
Lead can ...
Anodic protection54 has been successfully applied and is effective in controlling
corrosion of mild steel in storage tanks , etc . , in black as well as white
concentrated acids . Behaviour of sulphuric acid has attracted wide attention55 .
Lead can ...
Page 148
The greater resistance of these steels to atmosphere is broadly due to the fact
that the rust formed on them are highly adherent and impervious offering an
effective barrier against environment . It may be mentioned that no similar benefit
is ...
The greater resistance of these steels to atmosphere is broadly due to the fact
that the rust formed on them are highly adherent and impervious offering an
effective barrier against environment . It may be mentioned that no similar benefit
is ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
INTRODUCTION | 3 |
CHEMICAL CORROSION AND ITS PREVENTION | 13 |
DISCUSSION | 22 |
9 other sections not shown
Common terms and phrases
addition alloys aluminium ammonia ammonium amount anodic application attack bottom carbon steel cast iron cathodic protection cause chemical chloride chromium coatings concentration construction containing cooling corrosion problems corrosion rate cracking crude developed distillation effective environment epoxy equipment exchangers failure fertiliser flow give given handling heat hydrogen hydrogen sulphide increase industry inhibitor iron lead less material metal method mild steel Monel months natural observed occurred operating organic oxide oxygen paint petroleum phosphate pipe pitting plant plates potential practice presence pressure prevent pumps range reaction reduced refinery removal resistance rubber severe shell showing solution specially stainless steel steam storage tanks stress corrosion structure suitable sulphuric acid surface Table tanks temperature tests thickness tower treatment tubes unit various welding zinc
Bibliographic information
| Title | Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 |
| Editors | K. N. P. Rao, A. K. Lahiri |
| Contributor | Corrosion Advisory Bureau |
| Publisher | Corrosion Advisory Bureau, 1969 |
| Original from | the University of Wisconsin - Madison |
| Digitized | 27 Feb 2008 |
| Length | 159 pages |
| Export Citation | BiBTeX EndNote RefMan |