At the end of the test , glass - filled fibre glass reinforced epoxy gave the best
results as in addition to providing complete protection it bonded firmly with the
metal . This material was ultimately applied to the towers for corrosion protection .
At the end of the test , glass - filled fibre glass reinforced epoxy gave the best
results as in addition to providing complete protection it bonded firmly with the
metal . This material was ultimately applied to the towers for corrosion protection .
Page 118
The recent trend in the protection of storage tanks is the use of air drying linseed
or soyaesters of epoxy resins as priming and finishing coats for storage tanks and
structural steel works . White paints based on epoxy ester have the advantage ...
The recent trend in the protection of storage tanks is the use of air drying linseed
or soyaesters of epoxy resins as priming and finishing coats for storage tanks and
structural steel works . White paints based on epoxy ester have the advantage ...
Page 120
Storage tanks in airfields are protected by amine cured epoxy and polyurethane
coatings . I ir irg of rail tank wagons , road lorries and aircraft fuellers with similar
type of paint coatings , applied to a minimum thickness of 5 mils , has become the
...
Storage tanks in airfields are protected by amine cured epoxy and polyurethane
coatings . I ir irg of rail tank wagons , road lorries and aircraft fuellers with similar
type of paint coatings , applied to a minimum thickness of 5 mils , has become the
...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
INTRODUCTION | 3 |
CHEMICAL CORROSION AND ITS PREVENTION | 13 |
DISCUSSION | 22 |
9 other sections not shown
Common terms and phrases
addition alloys aluminium ammonia ammonium amount anodic application attack bottom carbon steel cast iron cathodic protection cause chemical chloride chromium coatings concentration construction containing cooling corrosion problems corrosion rate cracking crude developed distillation effective environment epoxy equipment exchangers failure fertiliser flow give given handling heat hydrogen hydrogen sulphide increase industry inhibitor iron lead less material metal method mild steel Monel months natural observed occurred operating organic oxide oxygen paint petroleum phosphate pipe pitting plant plates potential practice presence pressure prevent pumps range reaction reduced refinery removal resistance rubber severe shell showing solution specially stainless steel steam storage tanks stress corrosion structure suitable sulphuric acid surface Table tanks temperature tests thickness tower treatment tubes unit various welding zinc
Bibliographic information
| Title | Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 |
| Editors | K. N. P. Rao, A. K. Lahiri |
| Contributor | Corrosion Advisory Bureau |
| Publisher | Corrosion Advisory Bureau, 1969 |
| Original from | the University of Wisconsin - Madison |
| Digitized | 27 Feb 2008 |
| Length | 159 pages |
| Export Citation | BiBTeX EndNote RefMan |