Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968K. N. P. Rao, A. K. Lahiri |
From inside the book
Results 1-3 of 10
Page 18
... fabrication of equipments are susceptible to stress corrosion cracking to a greater or lesser degree . This type of attack takes place when a material is subjected to tensile stress and specific corrosive media , the type of media ...
... fabrication of equipments are susceptible to stress corrosion cracking to a greater or lesser degree . This type of attack takes place when a material is subjected to tensile stress and specific corrosive media , the type of media ...
Page 44
... fabrication to remove the hair line shrinkage cracks from the weld craters . It was not established what caused the ... fabricated from type 347 stainless steel . The vessel was exposed during intermittent operation to 11 M nitric acid ...
... fabrication to remove the hair line shrinkage cracks from the weld craters . It was not established what caused the ... fabricated from type 347 stainless steel . The vessel was exposed during intermittent operation to 11 M nitric acid ...
Page 72
... fabrication of reaction vessels has been observed . I feel that the problem is similar to what has been indicated by fellow delegates regarding experience in their plants . Dr. A. K. Lahiri ( Corrosion Advisory Bureau , Jamshedpur ) ...
... fabrication of reaction vessels has been observed . I feel that the problem is similar to what has been indicated by fellow delegates regarding experience in their plants . Dr. A. K. Lahiri ( Corrosion Advisory Bureau , Jamshedpur ) ...
Contents
INTRODUCTION | 3 |
CHEMICAL CORROSION AND ITS PREVENTION | 13 |
CORROSION PROBLEMS IN THE MANUFACTURE OF NITROGEN BASED FERTILIZER | 27 |
9 other sections not shown
Common terms and phrases
addition alloys aluminium ammonia ammonium amount anodic application attack bottom carbon steel cast iron cathodic protection cause chemical chloride chromium coatings concentration construction containing cooling corrosion problems corrosion rate cracking crude developed distillation effective environment epoxy equipment exchangers failure fertiliser flow formation give given handling heat higher hydrogen hydrogen sulphide increase industry inhibitor iron lead material metal method mild steel Monel months natural observed occurred operating organic oxide oxygen paint petroleum phosphate pipe pitting plant plates potential practice presence pressure prevent pumps range reaction reduced refinery removal resistance rubber severe shell showing solution specially stainless steel steam storage tanks stress corrosion structure suitable sulphuric acid surface Table tanks temperature tests thickness tower treatment tubes unit various welding zinc