Monel filter cloth for filtering of clay - treated acid stocks gives good life . In high
temperature use Hastelloy A and ... concentrated form and temperatures are low ,
mild steel equipments give satisfactory life . Where conditions of high velocity or ...
Monel filter cloth for filtering of clay - treated acid stocks gives good life . In high
temperature use Hastelloy A and ... concentrated form and temperatures are low ,
mild steel equipments give satisfactory life . Where conditions of high velocity or ...
Page 130
A large number of factors can give rise to variations in potential on a structure
immersed in water . Galvanic or two metal corrosion occurs , when dissimilar
metals are brought in electrical contact and when exposed to a corrosive
electrolyte .
A large number of factors can give rise to variations in potential on a structure
immersed in water . Galvanic or two metal corrosion occurs , when dissimilar
metals are brought in electrical contact and when exposed to a corrosive
electrolyte .
Page 150
Coatings of bitumen , coal tar or epoxy - coal tar give excellent protection to the
buried and the underwater structures . Now - a - days cathodic protection is also
extensively used for the underground and immersed structures . CORROSION
OF ...
Coatings of bitumen , coal tar or epoxy - coal tar give excellent protection to the
buried and the underwater structures . Now - a - days cathodic protection is also
extensively used for the underground and immersed structures . CORROSION
OF ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
INTRODUCTION | 3 |
CHEMICAL CORROSION AND ITS PREVENTION | 13 |
DISCUSSION | 22 |
9 other sections not shown
Common terms and phrases
addition alloys aluminium ammonia ammonium amount anodic application attack bottom carbon steel cast iron cathodic protection cause chemical chloride chromium coatings concentration construction containing cooling corrosion problems corrosion rate cracking crude developed distillation effective environment epoxy equipment exchangers failure fertiliser flow give given handling heat hydrogen hydrogen sulphide increase industry inhibitor iron lead less material metal method mild steel Monel months natural observed occurred operating organic oxide oxygen paint petroleum phosphate pipe pitting plant plates potential practice presence pressure prevent pumps range reaction reduced refinery removal resistance rubber severe shell showing solution specially stainless steel steam storage tanks stress corrosion structure suitable sulphuric acid surface Table tanks temperature tests thickness tower treatment tubes unit various welding zinc
Bibliographic information
| Title | Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 |
| Editors | K. N. P. Rao, A. K. Lahiri |
| Contributor | Corrosion Advisory Bureau |
| Publisher | Corrosion Advisory Bureau, 1969 |
| Original from | the University of Wisconsin - Madison |
| Digitized | 27 Feb 2008 |
| Length | 159 pages |
| Export Citation | BiBTeX EndNote RefMan |