Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 |
From inside the book
Results 1-3 of 26
Page 50
In one instance cast iron was replaced with durimet 20 in a submerged pump
handling strong acid . High silicon irons are also used for acid strengths below
100 % . Cast iron and high silicon irons should not be used for handling the
fuming ...
In one instance cast iron was replaced with durimet 20 in a submerged pump
handling strong acid . High silicon irons are also used for acid strengths below
100 % . Cast iron and high silicon irons should not be used for handling the
fuming ...
Page 95
Carbon steel pipe is satisfactory for handling conc . acid and welded or screwed
pipes are extensively used . Red brass and lead lined pipes are also employed
in handling dilute acid . For pumps and valves handling the acid sludge from the
...
Carbon steel pipe is satisfactory for handling conc . acid and welded or screwed
pipes are extensively used . Red brass and lead lined pipes are also employed
in handling dilute acid . For pumps and valves handling the acid sludge from the
...
Page 117
Corrosion Problem in Handling and Storage of Petroleum and Fertilizer Products
Industry R . K , BANERJEE AND C . P . De Naval Chemical and Metallurgical
Laboratory , Bombay AND INTRODUCTION Corrosion is a natural process of ...
Corrosion Problem in Handling and Storage of Petroleum and Fertilizer Products
Industry R . K , BANERJEE AND C . P . De Naval Chemical and Metallurgical
Laboratory , Bombay AND INTRODUCTION Corrosion is a natural process of ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
INTRODUCTION | 3 |
CHEMICAL CORROSION AND ITS PREVENTION | 13 |
DISCUSSION | 22 |
9 other sections not shown
Common terms and phrases
addition alloys aluminium ammonia ammonium amount anodic application attack bottom carbon steel cast iron cathodic protection cause chemical chloride chromium coatings concentration construction containing cooling corrosion problems corrosion rate cracking crude developed distillation effective environment epoxy equipment exchangers failure fertiliser flow give given handling heat hydrogen hydrogen sulphide increase industry inhibitor iron lead less material metal method mild steel Monel months natural observed occurred operating organic oxide oxygen paint petroleum phosphate pipe pitting plant plates potential practice presence pressure prevent pumps range reaction reduced refinery removal resistance rubber severe shell showing solution specially stainless steel steam storage tanks stress corrosion structure suitable sulphuric acid surface Table tanks temperature tests thickness tower treatment tubes unit various welding zinc
Bibliographic information
| Title | Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 |
| Editors | K. N. P. Rao, A. K. Lahiri |
| Contributor | Corrosion Advisory Bureau |
| Publisher | Corrosion Advisory Bureau, 1969 |
| Original from | the University of Wisconsin - Madison |
| Digitized | 27 Feb 2008 |
| Length | 159 pages |
| Export Citation | BiBTeX EndNote RefMan |