It has been found that a proper surface preparation followed by an application of
a thick coating of paint are adequate in preventing external corrosion of storage
tanks . It has further been established that corrosion in marine condition is not ...
It has been found that a proper surface preparation followed by an application of
a thick coating of paint are adequate in preventing external corrosion of storage
tanks . It has further been established that corrosion in marine condition is not ...
Page 118
For the white and other pestal shades , alkyd paints have also been used with
advantage . ... in the presence of gross chemical pollution of the atmosphere or
where spillage occurs resulting in the damage of the conventional paint systems .
For the white and other pestal shades , alkyd paints have also been used with
advantage . ... in the presence of gross chemical pollution of the atmosphere or
where spillage occurs resulting in the damage of the conventional paint systems .
Page 149
It has been found that the life of the paint coating on sand blasted surface is 4
times more effective than the paint applied on weathered steel . PAINTING Much
can be said on the selection of the paints , the basic requirement being to have ...
It has been found that the life of the paint coating on sand blasted surface is 4
times more effective than the paint applied on weathered steel . PAINTING Much
can be said on the selection of the paints , the basic requirement being to have ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
INTRODUCTION | 3 |
CHEMICAL CORROSION AND ITS PREVENTION | 13 |
DISCUSSION | 22 |
9 other sections not shown
Common terms and phrases
addition alloys aluminium ammonia ammonium amount anodic application attack bottom carbon steel cast iron cathodic protection cause chemical chloride chromium coatings concentration construction containing cooling corrosion problems corrosion rate cracking crude developed distillation effective environment epoxy equipment exchangers failure fertiliser flow give given handling heat hydrogen hydrogen sulphide increase industry inhibitor iron lead less material metal method mild steel Monel months natural observed occurred operating organic oxide oxygen paint petroleum phosphate pipe pitting plant plates potential practice presence pressure prevent pumps range reaction reduced refinery removal resistance rubber severe shell showing solution specially stainless steel steam storage tanks stress corrosion structure suitable sulphuric acid surface Table tanks temperature tests thickness tower treatment tubes unit various welding zinc
Bibliographic information
| Title | Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 |
| Editors | K. N. P. Rao, A. K. Lahiri |
| Contributor | Corrosion Advisory Bureau |
| Publisher | Corrosion Advisory Bureau, 1969 |
| Original from | the University of Wisconsin - Madison |
| Digitized | 27 Feb 2008 |
| Length | 159 pages |
| Export Citation | BiBTeX EndNote RefMan |