Page 117
... paint are adequate in preventing external corrosion of storage tanks . It has further been established that corrosion in marine condition is not only due to inadequate corrosion resistance of paint films but due to the faulty surface ...
... paint are adequate in preventing external corrosion of storage tanks . It has further been established that corrosion in marine condition is not only due to inadequate corrosion resistance of paint films but due to the faulty surface ...
Page 118
... paint has been found superior under tropical conditions . For the white and other pestal shades , alkyd paints have also been used with advantage . The recent trend in the protection of storage tanks is the use of air drying linseed or ...
... paint has been found superior under tropical conditions . For the white and other pestal shades , alkyd paints have also been used with advantage . The recent trend in the protection of storage tanks is the use of air drying linseed or ...
Page 149
... paint coating on sand blasted surface is 4 times more effective than the paint applied on weathered steel . PAINTING Much can be said on the selection of the paints , the basic requirement being to have excellent corrosion resistance ...
... paint coating on sand blasted surface is 4 times more effective than the paint applied on weathered steel . PAINTING Much can be said on the selection of the paints , the basic requirement being to have excellent corrosion resistance ...
Contents
INTRODUCTION | 3 |
CHEMICAL CORROSION AND ITS PREVENTION | 13 |
CORROSION PROBLEMS IN THE MANUFACTURE OF NITROGEN BASED FERTILIZER | 27 |
9 other sections not shown
Common terms and phrases
addition alloys aluminium ammonia ammonium amount anodic application attack bottom carbon steel cast iron cathodic protection cause chemical chloride chromium coatings concentration construction containing cooling corrosion problems corrosion rate cracking crude developed distillation effective environment epoxy equipment exchangers failure fertiliser flow formation give given handling heat higher hydrogen hydrogen sulphide increase industry inhibitor iron lead material metal method mild steel Monel months natural observed occurred operating organic oxide oxygen paint petroleum phosphate pipe pitting plant plates potential practice presence pressure prevent pumps range reaction reduced refinery removal resistance rubber severe shell showing solution specially stainless steel steam storage tanks stress corrosion structure suitable sulphuric acid surface Table tanks temperature tests thickness tower treatment tubes unit various welding zinc