Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 |
From inside the book
Results 1-3 of 34
Page 35
Severe corrosion of mild steel equipment has also been observed in the
degasification unit which follows the carbon dioxide scrubber . The corrosion has
been very severe in the Sindri Plant . In this section water , laden with carbon
dioxide , is ...
Severe corrosion of mild steel equipment has also been observed in the
degasification unit which follows the carbon dioxide scrubber . The corrosion has
been very severe in the Sindri Plant . In this section water , laden with carbon
dioxide , is ...
Page 91
brass is susceptible to dezincification and so has been replaced to a great extent
by aluminium brass and inhibited admiralty brass containing arsenic where the
conditions are less severe . Typical practice appears to have been to start out ...
brass is susceptible to dezincification and so has been replaced to a great extent
by aluminium brass and inhibited admiralty brass containing arsenic where the
conditions are less severe . Typical practice appears to have been to start out ...
Page 96
The principal use of this material has been for heat exchanger tubes in
applications where the acid concentrations may vary from dilute to anhydrous .
The austentitic stainless steels are subjected to severe corrosion by the hot acid
solutions ...
The principal use of this material has been for heat exchanger tubes in
applications where the acid concentrations may vary from dilute to anhydrous .
The austentitic stainless steels are subjected to severe corrosion by the hot acid
solutions ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
INTRODUCTION | 3 |
CHEMICAL CORROSION AND ITS PREVENTION | 13 |
DISCUSSION | 22 |
9 other sections not shown
Common terms and phrases
addition alloys aluminium ammonia ammonium amount anodic application attack bottom carbon steel cast iron cathodic protection cause chemical chloride chromium coatings concentration construction containing cooling corrosion problems corrosion rate cracking crude developed distillation effective environment epoxy equipment exchangers failure fertiliser flow give given handling heat hydrogen hydrogen sulphide increase industry inhibitor iron lead less material metal method mild steel Monel months natural observed occurred operating organic oxide oxygen paint petroleum phosphate pipe pitting plant plates potential practice presence pressure prevent pumps range reaction reduced refinery removal resistance rubber severe shell showing solution specially stainless steel steam storage tanks stress corrosion structure suitable sulphuric acid surface Table tanks temperature tests thickness tower treatment tubes unit various welding zinc
Bibliographic information
| Title | Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 |
| Editors | K. N. P. Rao, A. K. Lahiri |
| Contributor | Corrosion Advisory Bureau |
| Publisher | Corrosion Advisory Bureau, 1969 |
| Original from | the University of Wisconsin - Madison |
| Digitized | 27 Feb 2008 |
| Length | 159 pages |
| Export Citation | BiBTeX EndNote RefMan |