Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 |
From inside the book
Results 1-3 of 11
Page 60
3 Photograph of the failed 304 stainless steel strip in the unetched condition ,
showing numerous long cracks and honeycomb type cracking pattern . X115 M
US S FUSS Se SA SA . DIAS Meie Frien 4 3S. Fig . 4 Photomicrograph of the
failed ...
3 Photograph of the failed 304 stainless steel strip in the unetched condition ,
showing numerous long cracks and honeycomb type cracking pattern . X115 M
US S FUSS Se SA SA . DIAS Meie Frien 4 3S. Fig . 4 Photomicrograph of the
failed ...
Page 63
9 Photomicrograph of the failed m . s . header showing branched intergranular
cracking Nital Etch . Fig . 10 Photomicrograph of the failed m . s . tube showing
branched intergranular cracking . Nital Etch . X450 Fig . 13 Photograph of the ...
9 Photomicrograph of the failed m . s . header showing branched intergranular
cracking Nital Etch . Fig . 10 Photomicrograph of the failed m . s . tube showing
branched intergranular cracking . Nital Etch . X450 Fig . 13 Photograph of the ...
Page 66
Fig . 15 Photomicrograph of the cracked surface of the mild steel liquid ammonia
product pipe line showing the intergranular cracking pattern . Nital Etch . X340
FIG . 16 Photograph showing the fissures in the lagging on a decomposer unit .
Fig . 15 Photomicrograph of the cracked surface of the mild steel liquid ammonia
product pipe line showing the intergranular cracking pattern . Nital Etch . X340
FIG . 16 Photograph showing the fissures in the lagging on a decomposer unit .
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
INTRODUCTION | 3 |
CHEMICAL CORROSION AND ITS PREVENTION | 13 |
DISCUSSION | 22 |
9 other sections not shown
Common terms and phrases
addition alloys aluminium ammonia ammonium amount anodic application attack bottom carbon steel cast iron cathodic protection cause chemical chloride chromium coatings concentration construction containing cooling corrosion problems corrosion rate cracking crude developed distillation effective environment epoxy equipment exchangers failure fertiliser flow give given handling heat hydrogen hydrogen sulphide increase industry inhibitor iron lead less material metal method mild steel Monel months natural observed occurred operating organic oxide oxygen paint petroleum phosphate pipe pitting plant plates potential practice presence pressure prevent pumps range reaction reduced refinery removal resistance rubber severe shell showing solution specially stainless steel steam storage tanks stress corrosion structure suitable sulphuric acid surface Table tanks temperature tests thickness tower treatment tubes unit various welding zinc
Bibliographic information
| Title | Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 |
| Editors | K. N. P. Rao, A. K. Lahiri |
| Contributor | Corrosion Advisory Bureau |
| Publisher | Corrosion Advisory Bureau, 1969 |
| Original from | the University of Wisconsin - Madison |
| Digitized | 27 Feb 2008 |
| Length | 159 pages |
| Export Citation | BiBTeX EndNote RefMan |