Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 |
From inside the book
Results 1-3 of 47
Page 19
Stainless Steel - Austenitic Austenitic stainless steels readily fail by stress
corrosion cracking , specially in presence of chlorides . Cracking in alkali and 12
% HF & 0 . 2 % H FSiO6 has also been reported . The stress required for cracking
is ...
Stainless Steel - Austenitic Austenitic stainless steels readily fail by stress
corrosion cracking , specially in presence of chlorides . Cracking in alkali and 12
% HF & 0 . 2 % H FSiO6 has also been reported . The stress required for cracking
is ...
Page 45
The tubes were of type 347 stainless steel . The heat exchanger tubes were
subsequently embrittled . By incorporating an oil filter the trouble was overcome .
Metals which were most frequently used in nitric acid and ammonium nitrate ...
The tubes were of type 347 stainless steel . The heat exchanger tubes were
subsequently embrittled . By incorporating an oil filter the trouble was overcome .
Metals which were most frequently used in nitric acid and ammonium nitrate ...
Page 131
Table 1 Galvanic series of some commercial metals and alloys in sea water
Noble or cathodic Platinum Gold Graphite Titanium Silver ( Chlorimet 3 ( 62 Ni ,
18 Cr , 18 Mo ) ( Hastelloy C ( 62 Ni , 17 Cr , 15 Mo ) ( 18 - 8 Mo stainless steel ...
Table 1 Galvanic series of some commercial metals and alloys in sea water
Noble or cathodic Platinum Gold Graphite Titanium Silver ( Chlorimet 3 ( 62 Ni ,
18 Cr , 18 Mo ) ( Hastelloy C ( 62 Ni , 17 Cr , 15 Mo ) ( 18 - 8 Mo stainless steel ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
INTRODUCTION | 3 |
CHEMICAL CORROSION AND ITS PREVENTION | 13 |
DISCUSSION | 22 |
9 other sections not shown
Common terms and phrases
addition alloys aluminium ammonia ammonium amount anodic application attack bottom carbon steel cast iron cathodic protection cause chemical chloride chromium coatings concentration construction containing cooling corrosion problems corrosion rate cracking crude developed distillation effective environment epoxy equipment exchangers failure fertiliser flow give given handling heat hydrogen hydrogen sulphide increase industry inhibitor iron lead less material metal method mild steel Monel months natural observed occurred operating organic oxide oxygen paint petroleum phosphate pipe pitting plant plates potential practice presence pressure prevent pumps range reaction reduced refinery removal resistance rubber severe shell showing solution specially stainless steel steam storage tanks stress corrosion structure suitable sulphuric acid surface Table tanks temperature tests thickness tower treatment tubes unit various welding zinc
Bibliographic information
| Title | Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 |
| Editors | K. N. P. Rao, A. K. Lahiri |
| Contributor | Corrosion Advisory Bureau |
| Publisher | Corrosion Advisory Bureau, 1969 |
| Original from | the University of Wisconsin - Madison |
| Digitized | 27 Feb 2008 |
| Length | 159 pages |
| Export Citation | BiBTeX EndNote RefMan |