Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968K. N. P. Rao, A. K. Lahiri |
From inside the book
Results 1-3 of 30
Page 19
... Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 K. N. P. Rao, A. K. Lahiri. In actual practice the stress may be created by either residual internal stresses or by external applied stress . The corrosive agent ...
... Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 K. N. P. Rao, A. K. Lahiri. In actual practice the stress may be created by either residual internal stresses or by external applied stress . The corrosive agent ...
Page 20
... stress corrosion cracking under certain conditions of heat treatment . This type of failure is also encountered in other low alloy high strength steel where the required mechanical property is obtained ... stress corrosion . It is not a 20.
... stress corrosion cracking under certain conditions of heat treatment . This type of failure is also encountered in other low alloy high strength steel where the required mechanical property is obtained ... stress corrosion . It is not a 20.
Page 21
Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 K. N. P. Rao, A. K. Lahiri. ful deterrent to stress corrosion . It ...
Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 K. N. P. Rao, A. K. Lahiri. ful deterrent to stress corrosion . It ...
Contents
INTRODUCTION | 3 |
CHEMICAL CORROSION AND ITS PREVENTION | 13 |
CORROSION PROBLEMS IN THE MANUFACTURE OF NITROGEN BASED FERTILIZER | 27 |
9 other sections not shown
Common terms and phrases
addition alloys aluminium ammonia ammonium amount anodic application attack bottom carbon steel cast iron cathodic protection cause chemical chloride chromium coatings concentration construction containing cooling corrosion problems corrosion rate cracking crude developed distillation effective environment epoxy equipment exchangers failure fertiliser flow formation give given handling heat higher hydrogen hydrogen sulphide increase industry inhibitor iron lead material metal method mild steel Monel months natural observed occurred operating organic oxide oxygen paint petroleum phosphate pipe pitting plant plates potential practice presence pressure prevent pumps range reaction reduced refinery removal resistance rubber severe shell showing solution specially stainless steel steam storage tanks stress corrosion structure suitable sulphuric acid surface Table tanks temperature tests thickness tower treatment tubes unit various welding zinc