Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 |
From inside the book
Results 1-3 of 24
Page 21
Tests on the effect of leachings from a number of commercial insulations showed
stress corrosion could be produced in all ... But such preventive measures should
be checked in controlled tests first , since a control that seems theoretically ...
Tests on the effect of leachings from a number of commercial insulations showed
stress corrosion could be produced in all ... But such preventive measures should
be checked in controlled tests first , since a control that seems theoretically ...
Page 32
A ' NACE task group on high sulphide corrosion in catalytic reformers tested a
number of materials of construction for service at 1495 ... Average Conditions
Test 1 Test 2 1495 Temperature °F Hydrogen Pressure H , S in hydrogen by vol .
A ' NACE task group on high sulphide corrosion in catalytic reformers tested a
number of materials of construction for service at 1495 ... Average Conditions
Test 1 Test 2 1495 Temperature °F Hydrogen Pressure H , S in hydrogen by vol .
Page 54
Several materials were tested but no conclusion could be reached . Exposure
tests did not indicate any difference between the service life of seamless or
welded high nickel tubes . Field experience showed them to be more suitable at
higher ...
Several materials were tested but no conclusion could be reached . Exposure
tests did not indicate any difference between the service life of seamless or
welded high nickel tubes . Field experience showed them to be more suitable at
higher ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
INTRODUCTION | 3 |
CHEMICAL CORROSION AND ITS PREVENTION | 13 |
DISCUSSION | 22 |
9 other sections not shown
Common terms and phrases
addition alloys aluminium ammonia ammonium amount anodic application attack bottom carbon steel cast iron cathodic protection cause chemical chloride chromium coatings concentration construction containing cooling corrosion problems corrosion rate cracking crude developed distillation effective environment epoxy equipment exchangers failure fertiliser flow give given handling heat hydrogen hydrogen sulphide increase industry inhibitor iron lead less material metal method mild steel Monel months natural observed occurred operating organic oxide oxygen paint petroleum phosphate pipe pitting plant plates potential practice presence pressure prevent pumps range reaction reduced refinery removal resistance rubber severe shell showing solution specially stainless steel steam storage tanks stress corrosion structure suitable sulphuric acid surface Table tanks temperature tests thickness tower treatment tubes unit various welding zinc
Bibliographic information
| Title | Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 |
| Editors | K. N. P. Rao, A. K. Lahiri |
| Contributor | Corrosion Advisory Bureau |
| Publisher | Corrosion Advisory Bureau, 1969 |
| Original from | the University of Wisconsin - Madison |
| Digitized | 27 Feb 2008 |
| Length | 159 pages |
| Export Citation | BiBTeX EndNote RefMan |