Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 |
From inside the book
Results 1-3 of 8
Page 16
... the fact that some metals like steel , stainless steel , titanium , etc . can form a
protective , passive oxide layer when their potential is raised to a suitable value
in the anodic direction and maintained at that value by a constant flow of current .
... the fact that some metals like steel , stainless steel , titanium , etc . can form a
protective , passive oxide layer when their potential is raised to a suitable value
in the anodic direction and maintained at that value by a constant flow of current .
Page 40
Titanium alloyed low alloy steels are also good but the titanium content should
have the minimum excess above that necessary for stabilisation otherwise
nitriding would be serious . Tungsten imparts greater hot strength but leads to
severe ...
Titanium alloyed low alloy steels are also good but the titanium content should
have the minimum excess above that necessary for stabilisation otherwise
nitriding would be serious . Tungsten imparts greater hot strength but leads to
severe ...
Page 46
Titanium has also been used as a constructional material . Spencer Chemical Co
in its Vicksbrough , Mississippi , plant had a nitric acid cooler condenser having
tubes of type 304 stainless steel but service was interrupted every 18 months for
...
Titanium has also been used as a constructional material . Spencer Chemical Co
in its Vicksbrough , Mississippi , plant had a nitric acid cooler condenser having
tubes of type 304 stainless steel but service was interrupted every 18 months for
...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
INTRODUCTION | 3 |
CHEMICAL CORROSION AND ITS PREVENTION | 13 |
DISCUSSION | 22 |
9 other sections not shown
Common terms and phrases
addition alloys aluminium ammonia ammonium amount anodic application attack bottom carbon steel cast iron cathodic protection cause chemical chloride chromium coatings concentration construction containing cooling corrosion problems corrosion rate cracking crude developed distillation effective environment epoxy equipment exchangers failure fertiliser flow give given handling heat hydrogen hydrogen sulphide increase industry inhibitor iron lead less material metal method mild steel Monel months natural observed occurred operating organic oxide oxygen paint petroleum phosphate pipe pitting plant plates potential practice presence pressure prevent pumps range reaction reduced refinery removal resistance rubber severe shell showing solution specially stainless steel steam storage tanks stress corrosion structure suitable sulphuric acid surface Table tanks temperature tests thickness tower treatment tubes unit various welding zinc
Bibliographic information
| Title | Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968 |
| Editors | K. N. P. Rao, A. K. Lahiri |
| Contributor | Corrosion Advisory Bureau |
| Publisher | Corrosion Advisory Bureau, 1969 |
| Original from | the University of Wisconsin - Madison |
| Digitized | 27 Feb 2008 |
| Length | 159 pages |
| Export Citation | BiBTeX EndNote RefMan |