Corrosion in Fertiliser and Petroleum Industry: Proceedings of Short Course on "Corrosion in Fertiliser and Petroleum Industry" Organised by the Corrosion Advisory Bureau at Udyogamandal from 20th to 24th December 1968K. N. P. Rao, A. K. Lahiri |
From inside the book
Results 1-3 of 7
Page 40
... Titanium alloyed low alloy steels are also good but the titanium content should have the minimum excess above that necessary for stabilisation otherwise nitriding would be serious . Tungsten imparts greater hot strength but leads to ...
... Titanium alloyed low alloy steels are also good but the titanium content should have the minimum excess above that necessary for stabilisation otherwise nitriding would be serious . Tungsten imparts greater hot strength but leads to ...
Page 46
... titanium seamless tube brought gratifying results . In another New Jersey Plant the glass lined storage tank for nitric acid was failing frequently and it was changed to titanium . The tank cost 2.5 to 3 tonnes more than glass lined ...
... titanium seamless tube brought gratifying results . In another New Jersey Plant the glass lined storage tank for nitric acid was failing frequently and it was changed to titanium . The tank cost 2.5 to 3 tonnes more than glass lined ...
Page 149
... titanium dioxide . While for the prime coat importance is given on pigments having corrosion inhibitive properties , in the case of top coats the emphasis is put on the selection of vehicle or binder .. Oil base or oleo - resin paint is ...
... titanium dioxide . While for the prime coat importance is given on pigments having corrosion inhibitive properties , in the case of top coats the emphasis is put on the selection of vehicle or binder .. Oil base or oleo - resin paint is ...
Contents
INTRODUCTION | 3 |
CHEMICAL CORROSION AND ITS PREVENTION | 13 |
CORROSION PROBLEMS IN THE MANUFACTURE OF NITROGEN BASED FERTILIZER | 27 |
9 other sections not shown
Common terms and phrases
addition alloys aluminium ammonia ammonium amount anodic application attack bottom carbon steel cast iron cathodic protection cause chemical chloride chromium coatings concentration construction containing cooling corrosion problems corrosion rate cracking crude developed distillation effective environment epoxy equipment exchangers failure fertiliser flow formation give given handling heat higher hydrogen hydrogen sulphide increase industry inhibitor iron lead material metal method mild steel Monel months natural observed occurred operating organic oxide oxygen paint petroleum phosphate pipe pitting plant plates potential practice presence pressure prevent pumps range reaction reduced refinery removal resistance rubber severe shell showing solution specially stainless steel steam storage tanks stress corrosion structure suitable sulphuric acid surface Table tanks temperature tests thickness tower treatment tubes unit various welding zinc