... coating system capable of withstanding the high contact loads associated with reeling were all particularly expensive . Because of this , the cost benefits of reeling could not be fully realised for insulated pipelines . The successful ...
... coating system capable of withstanding the high contact loads associated with reeling were all particularly expensive . Because of this , the cost benefits of reeling could not be fully realised for insulated pipelines . The successful ...
Page 140
... coating failure is then determined . Specimens A , C and F were tested . The criterion for coating failure was perforation of the coating . Thermal Cycling Stress Test . To determine the susceptibility of the PUFI to failure under ...
... coating failure is then determined . Specimens A , C and F were tested . The criterion for coating failure was perforation of the coating . Thermal Cycling Stress Test . To determine the susceptibility of the PUFI to failure under ...
Page 141
... coating of Specimen E was below that specified ( 7-9mm total thickness ) . Both the PUFI and EPU were below thickness . The total thickness of coatings ( PUFI and PE ) of Specimen F was 9-11mm . The PE coating was typically 2mm ...
... coating of Specimen E was below that specified ( 7-9mm total thickness ) . Both the PUFI and EPU were below thickness . The total thickness of coatings ( PUFI and PE ) of Specimen F was 9-11mm . The PE coating was typically 2mm ...
Contents
Design of the Troll Multiphase Transport System | 1 |
Propagation and Diffraction of Cnoidal Waves | 9 |
Dynamic Stresses and Motions of Offshore Pipelines During Laying | 17 |
Copyright | |
25 other sections not shown
Other editions - View all
Common terms and phrases
applied axial base metal brazing cables calculated carbon equivalent chemical composition cnoidal waves coating cooling crack curve cycle defects developed dew point temperature diameter dynamic tension force effect electrode equation failure field Figure fitness-for-purpose flaws flow foam forge welding fracture fracture mechanics free span frequency friction welding gas pipeline glycol GMAW Gr.B HAZ hardness heat input hydrocarbon dew point induction heating inner pipe installation insulation J-Lay length line pipe linepipe load material maximum measured mechanical properties method nonlinear offshore pipelines operation parameters pipe material pipe wall pipeline Pipeline Technology ASME plate pressure problem procedure propagation PUFI PWHT reeling S-N curves seam weld simulation Specimen steel stress surface T-cross portion tensile strength thermal thermal insulation toughness tube UOE pipe velocity wall thickness water depth water dew point weld metal X80 grade yield strength