Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 10, Part 5American Society of Mechanical Engineers, 1991 - Arctic regions |
From inside the book
Results 1-3 of 31
Page 73
... composition can give good notch toughness and bending ductility to ERW pipes . ( 6 ) The reel barge laying technique is thereby reliably applicable to the above improved ERW linepipes . Table 1 Pipe No. Grade 1 chemical composition ( wt ...
... composition can give good notch toughness and bending ductility to ERW pipes . ( 6 ) The reel barge laying technique is thereby reliably applicable to the above improved ERW linepipes . Table 1 Pipe No. Grade 1 chemical composition ( wt ...
Page 89
... composition of the weld metal within a narrow range as discussed above . To this end , new submerged - arc welding consumables ( flux and wire ) were developed . The important point in the weld metal chemical composition is that the ...
... composition of the weld metal within a narrow range as discussed above . To this end , new submerged - arc welding consumables ( flux and wire ) were developed . The important point in the weld metal chemical composition is that the ...
Page 95
... composition for X70 grade steel was finally determined through a trial production test described later . From the results , it was confirmed that chemical composition of Steel D in Table 3 was appropriate for X70 grade steel . Fig.3 ...
... composition for X70 grade steel was finally determined through a trial production test described later . From the results , it was confirmed that chemical composition of Steel D in Table 3 was appropriate for X70 grade steel . Fig.3 ...
Contents
Design of the Troll Multiphase Transport System | 1 |
Propagation and Diffraction of Cnoidal Waves | 9 |
Dynamic Stresses and Motions of Offshore Pipelines During Laying | 17 |
Copyright | |
25 other sections not shown
Other editions - View all
Common terms and phrases
applied axial base metal brazing cables calculated carbon equivalent chemical composition cnoidal waves coating cooling crack curve cycle defects developed dew point temperature diameter dynamic tension force effect electrode equation failure field Figure fitness-for-purpose flaws flow foam forge welding fracture fracture mechanics free span frequency friction welding gas pipeline glycol GMAW Gr.B HAZ hardness heat input hydrocarbon dew point induction heating inner pipe installation insulation J-Lay length line pipe linepipe load material maximum measured mechanical properties method nonlinear offshore pipelines operation parameters pipe material pipe wall pipeline Pipeline Technology ASME plate pressure problem procedure propagation PUFI PWHT reeling S-N curves seam weld simulation Specimen steel stress surface T-cross portion tensile strength thermal thermal insulation toughness tube UOE pipe velocity wall thickness water depth water dew point weld metal X80 grade yield strength