... tensile strength Re ... ≈ 500 N / mm2 and R. ≈600 N / mm2 respectively were evaluated ( arrow marked levels in Fig . 1 ) . The toughness behaviour , the yield to tensile ratio and the elongation are comparable to the results obtained ...
... tensile strength Re ... ≈ 500 N / mm2 and R. ≈600 N / mm2 respectively were evaluated ( arrow marked levels in Fig . 1 ) . The toughness behaviour , the yield to tensile ratio and the elongation are comparable to the results obtained ...
Page 64
... tensile strength of the plate were also examined . Fig.2 summarizes the relationship between carbon equivalent ( Ceq ) , as determined using the IIW formula , and tensile strength of plates manufactured by ICR and OLAC process . The tensile ...
... tensile strength of the plate were also examined . Fig.2 summarizes the relationship between carbon equivalent ( Ceq ) , as determined using the IIW formula , and tensile strength of plates manufactured by ICR and OLAC process . The tensile ...
Page 65
... tensile tested specimens of weldment more welded joint shows to be a lesser value than that of base metal . From the figure , it is understood that Ceq value of 0.38 is required to get weldment tensile strength to be equal or more than ...
... tensile tested specimens of weldment more welded joint shows to be a lesser value than that of base metal . From the figure , it is understood that Ceq value of 0.38 is required to get weldment tensile strength to be equal or more than ...
Contents
Propagation and Diffraction of Cnoidal Waves | 9 |
Dynamic Stresses and Motions of Offshore Pipelines During Laying | 17 |
TimeDevelopment of Scour Induced Free Spans of Pipelines | 25 |
Copyright | |
22 other sections not shown
Other editions - View all
Common terms and phrases
applied axial base metal brazing cables calculated carbon equivalent chemical composition cnoidal waves coating cooling crack CTOD curve cycle defects developed dew point temperature diameter dynamic tension force effect electrode equation field Figure fitness-for-purpose flaws flow foam forge welding fracture fracture mechanics free span frequency friction welding gas pipeline GMAW Gr.B HAZ hardness heat input hydrocarbon dew point induction heating inner pipe installation insulation internal J-Lay length line pipe linepipe load material maximum measured mechanical properties method microstructure nonlinear offshore pipelines operation ovalization parameters pipe material pipe wall pipeline plate pressure problem procedure propagation PUFI PWHT ratio reeling S-N curves seam weld simulation Specimen steel stress surface T-cross portion tensile strength thermal thermal insulation toughness tube UOE pipe velocity wall thickness water depth water dew point weld metal X80 grade yield strength