... weld- ing process , using consumables containing titanium- boron6,7 ) . A study was made on the technology which can concurrently achieve low hardenability and high toughness in the titanium ... weld metal . VE - 30 ( J ) 120 100 300 200 87.
... weld- ing process , using consumables containing titanium- boron6,7 ) . A study was made on the technology which can concurrently achieve low hardenability and high toughness in the titanium ... weld metal . VE - 30 ( J ) 120 100 300 200 87.
Page 89
... welds and maximum HAZ hardness on submerged - arc weld side in T - cross portion of UOE pipe . simultaneously achieve low hardenability and high tough- ness in the seam weld metal , the carbon , boron , oxygen , and nitrogen content ...
... welds and maximum HAZ hardness on submerged - arc weld side in T - cross portion of UOE pipe . simultaneously achieve low hardenability and high tough- ness in the seam weld metal , the carbon , boron , oxygen , and nitrogen content ...
Page 96
Selection of Welding Material As seam weld metal is heat treated as mentioned above , it is necessary to design a chemical composition suited for the heat treated weld metal . Since SAW weld metals contain a large amount of oxygen ...
Selection of Welding Material As seam weld metal is heat treated as mentioned above , it is necessary to design a chemical composition suited for the heat treated weld metal . Since SAW weld metals contain a large amount of oxygen ...
Contents
Design of the Troll Multiphase Transport System | 1 |
Propagation and Diffraction of Cnoidal Waves | 9 |
Dynamic Stresses and Motions of Offshore Pipelines During Laying | 17 |
Copyright | |
25 other sections not shown
Other editions - View all
Common terms and phrases
applied axial base metal brazing cables calculated carbon equivalent chemical composition cnoidal waves coating cooling crack curve cycle defects developed dew point temperature diameter dynamic tension force effect electrode equation failure field Figure fitness-for-purpose flaws flow foam forge welding fracture fracture mechanics free span frequency friction welding gas pipeline glycol GMAW Gr.B HAZ hardness heat input hydrocarbon dew point induction heating inner pipe installation insulation J-Lay length line pipe linepipe load material maximum measured mechanical properties method nonlinear offshore pipelines operation parameters pipe material pipe wall pipeline Pipeline Technology ASME plate pressure problem procedure propagation PUFI PWHT reeling S-N curves seam weld simulation Specimen steel stress surface T-cross portion tensile strength thermal thermal insulation toughness tube UOE pipe velocity wall thickness water depth water dew point weld metal X80 grade yield strength